This Article Full Text (PDF) All Versions of this Article: 0954008309339935v1 0954008309339935v2 21/5/653    most recent References Alert me when this article is cited Alert me if a correction is posted Services Email this article to a friend Similar articles in this journal Alert me to new issues of the journal Add to Saved Citations Download to citation manager Request Permissions Request Reprints Add to My Marked Citations Citing Articles Citing Articles via Scopus Google Scholar Articles by Ghose, S. Articles by Lineberry, Q. J. Social Bookmarking                         What's this?

High Temperature VARTM of Phenylethynyl Terminated Imides

National Institute of Aerospace, Hampton, VA 23666-6147, USA, sayata.ghose-1{at}nasa.gov

Kent A. Watson

National Institute of Aerospace, Hampton, VA 23666-6147, USA

Roberto J. Cano

NASA Langley Research Center, Hampton, VA 23681-2199, USA

Sean M. Britton

NASA Langley Research Center, Hampton, VA 23681-2199, USA

Brian J. Jensen

NASA Langley Research Center, Hampton, VA 23681-2199, USA

John W. Connell

NASA Langley Research Center, Hampton, VA 23681-2199, USA

Helen M. Herring

Lockheed Martin Engineering & Sciences Company, Hampton, VA 23666, USA

Quentin J. Lineberry

NASA GSRP at Western Kentucky University, Bowling Green, KY 42101, USA

Depending on the part type and quantity, fabrication of composite structures using vacuum-assisted resin transfer molding (VARTM) can be more affordable than conventional autoclave techniques. Recent efforts have focused on adapting VARTM for the fabrication of high temperature composites. Due to their low melt viscosity and long melt stability, certain phenylethynyl terminated imides (PETI) can be processed into composites using high temperature VARTM (HT-VARTM). However, one of the disadvantages of the current HT-VARTM resin systems has been the high porosity of the resultant composites. For aerospace applications, the desired void fraction of less than 2% has not yet been achieved. In the current study, two PETI resins, LaRC PETI-330 and LaRC PETI-8 have been used to make test specimens using HT-VARTM. The resins were infused into ten layers of IM7-6K carbon fiber 5-harness satin fabric at 260 or 280 ^°C and cured at temperature up to 371 °C. Initial runs yielded composites with high void content, typically greater than 7% by weight. A thermogravimetric-mass spectroscopic study was conducted to determine the source of volatiles leading to high porosity. It was determined that under the thermal cycle used for laminate fabrication, the phenylethynyl endcap was undergoing degradation leading to volatile evolution. This finding was unexpected as high quality composite laminates have been fabricated under higher pressures using these resin systems. The amount of weight loss experienced during the thermal cycle was only about 1% by weight, but this led to a significant amount of volatiles in a closed system. By modifying the thermal cycle used in laminate fabrication, the void content was significantly reduced (typically ~ 3% or less). The results of this work are presented herein.

Key Words: phenylethynyl terminated imides • VARTM • voids • acid digestion

This version was published on October 1, 2009

High Performance Polymers, Vol. 21, No. 5, 653-672 (2009)